In my project of renovating an elderly Wots Wot,the main problem is fuel soaking at the nose. Many joints have failed and ply doubles have delaminated. Has anyone succeeded in regluing ply pieces after they become fuel contaminated, maybe after cleaning with acetone or meths?

Link to comment
Share on other sites

Advert


interesting, though for the cost of the special glue I'd rather cut in a new bit of wood. Use the old bits to make a pattern.

The technique I've used in the past to extract the oil is to mix up a paste of meths and talc, spread on the affected area and leave to dry. This wicks the oil into the talc which you can then scrape off. Repeat if necessary. Works well enough for re-covering but I'm not sure I'd trust it for re-gluing structural stuff.

Link to comment
Share on other sites

Trouble is with these special use glues, is the manufacturer will tell you, test to see if it's fit for your particular use. I once many years ago had the joy of watching a motor rip free from an ancient flying dog of a machine.

The motor landed on a big stone, and the dog of an airframe didn't Evan (even) have the decency to wreck itself.

New wood makes sense.

Hate spellcheckers.

Edited By Don Fry on 08/05/2019 20:43:03

Link to comment
Share on other sites

Started removing affected parts of nose.

img_20190508_125155.jpg

Removing balsa sides

img_20190509_102951.jpg

Inner ply doublers damaged and joints to formers loose due to fuel seepage.

img_20190509_120531.jpg

Attempting to trace outline of doubles.

img_20190509_123516.jpg

Taking back balsa to sound wood and leaving suitable joining locations for new wood.

img_20190509_133121.jpg

Lots of work. A new fuse is £71... too easy. I paid less than that for the whole airframe with servos and ASP FS80.

Link to comment
Share on other sites

If it's not too late measure the downthrust and sidethrust used. Making a master template in cheap 3mm ply with both wing seats and cabane and engine bulkhead in correct alignment would help a lot now. Geting the cut outs in doubler is less important. Paper templates especially those with cutouts are too easily distorted, so ply is better than paper or cardboard.

Edited By kc on 09/05/2019 18:00:23

Link to comment
Share on other sites

Perhaps I should explain a bit more about making a master template. I once had a fuselage that had an even worse affliction than oil soakage - it had woodworm! Fortunately only the fuselage was affected and wings and tailplane were OK. Lacking the plan I used a balsa sheet that fitted onto the tailplane and then was located along the top fuselage edge, then the wing seat cut out was carefully drawn onto the balsa and bulkheads positions marked. Then this balsa was shaped to the wing seat and used as a template to produce two identical new fuselage sides. All the old wormy bits were then cut away and new fuselage produced from the template instead of a plan. Replicating the structure was not quite as important as getting the wing acurately located in relation to tailplane. With a biplane getting it also located in relation to the top wing would be important too..

Link to comment
Share on other sites

Thanks for that advice. I shall attempt to ensure the wing incidence, down and sidethrust are maintained. At present I am retaining all the important bits on one side while I repair the other, then work on the better side after. I believe I can get away without removing bulkheads or formers. I aim to use additional internal strengthening to make the original structural joints less important if they are less strong than originally.

Link to comment
Share on other sites

Template in 3mm ply for the new doubler being sized up

Interestingly, as others pointed out, the new ply also has a waxy feel and will need cleaning and roughing before gluing. I'd be surprised if they do that in the factory with artf construction. I also noticed the charred laser cut edges of formers don't seem to bond well.

img_20190509_220946.jpg

Link to comment
Share on other sites

Wow Phil, you are an artist

This job will be stronger than the original, and an abject lesson in repair work

And Yes, laser cut joints need attention, as vaporised wood dust contaminates joints

As you suggest, clean up joint faces to leave micro open pores in the cellulose (wood)

Following you with great interest

Link to comment
Share on other sites

That's a very neat bit of work! Of course keep a template in case of any further 'incidence' is a good idea. Same as when starting a kit - drawing around every component onto paper and noting material is a good insurance.

I looked up the component shapes ( actual photo copies ) of a Wots Wot kit and its very different to Phil's model which must have been a later kit or a Ready Built model.

Ply manufacturers deny that there is any release agent used but it's the heat glazed the surface.   I have never had a problem with ply doubler to balsa joints, but then I always used Thixofix or sometimes Glue Film.  Perhaps that's why instructions usually say use contact adhesive rather than PVA etc for doublers  -the rubbery type of contact adhesives sticks well to ply without any preparation.

Edited By kc on 10/05/2019 11:24:46

Link to comment
Share on other sites

I didn't know Thixofix was still about Glue Film never heard of it. The point is these adhesives contain their own solvent so deal with the waxy surfaces automatically so to speak. I think it is actually oils etc in the wood drawn to the surface and baked into the waxy film we find.on the surface. So yer pays yer pennies an' makes yer choice. Contact types or thinners etc and wood glues. I got a few samples of ply from Enricio Iglesias (Julio's cousin) via this forum but can't find the thread now.. He sent me some useable samples of quite a dark 3 ply about 1/8th thick. Very rigid but no apparent oils/waxes on the surface. Not had a chance to use it yet He was offering it for sale BTW

Link to comment
Share on other sites

Not much time today. Cut out lightening holes in the doubler.

img_20190510_214337.jpg

Checked fit before removing last bits of damaged doubler.

img_20190510_214350.jpg

These parts were well glued.

Drew round for second doubler. Now need final fit of first doubler.

img_20190510_214704.jpg

Doing the tab cut outs without Cad is patient work, hopefully, worth it to retain joint strength.

Link to comment
Share on other sites

Where I'm cutting through sound joints some seem to be cyano, which leaves a crisp residue, whilst the better ones have a flexible residue such as PVA might leave. I worked for Dunlop Research in the days when we invented Thixofix. We all knew it was rubbish, less strong than Evostick, but the thixotropic idea was a brilliant marketing idea and it sold well. You couldnt really build like this from scratch without laser cutting as the intricate ply jigsaw pieces are very time consuming.

I experimented with gluing some of the old bits back together. The worst of the contaminated parts I put back together with Pu glue, clamped overnight, no preparation such as cleaning or scraping! Resulting joint when set was pretty good, you could break it apart, but with some structural care and cleaning prep I think it will be OK. Interestingly I put 2 ply offcuts, sanded and cleaned, together with medium cyano, overnight. Next morning joint failed dismally. I don't think cyano is any good for ply.

Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.
Note: Your post will require moderator approval before it will be visible.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

 Share

×
×
  • Create New...